TAPPI T 702 om-14

TAPPI T 702 om-14

Click here to purchase
In extrusion coating a thin molten polymer film is coated on some kind of substrate. At highextrusion coating speed, even a minor disturbance on the melt web causes major quality problems, which veryrapidly lead to large quantities of waste. Therefore, higher coating speeds require polymers with high and evenquality in order to avoid waste due to polymer edge instability and web break.

The rheology-related phenomena that may cause problems in extrusion coating are neck-in (NI) anddraw-down (DD). The neck-in is the reduction of the film width and may cause uncoated areas on the substrate. Theneck-in is less if the melt elasticity is high. The draw-down is the ability of the melt to be drawn to thin filmswithout breaking. Draw-down is favored by a melt that is more viscous than elastic.

In optimizing the extrusion coating processing performance it is of utmost importance to balance the rheology of the polymer. This method describes how rheological measurements can be used to characterize LDPE. The storage modulus and zero shear viscosity have been found to be useful parameters to predict the extrusion coating performance of LDPE.

Product Details

Published:
12/01/2014
ANSI:
ANSI Approved
Number of Pages:
4
File Size:
1 file , 90 KB
Redline File Size:
2 files , 3.1 MB

You may also like

TAPPI T275 sp-23

TAPPI T275 sp-23

Screening of pulp (Somerville-type equipment)standard by Technical Association of the Pulp and Paper Industry, 06/01/2023

TAPPI TIP 0402-32

TAPPI TIP 0402-32

Guidelines for Thermal Spray Coatings Installed to Prevent Corrosion in Pulp Mill Process Equipmentstandard by Technical Association of the Pulp...

TAPPI T271 om-23

TAPPI T271 om-23

Fiber Lenth of Pulp and Paper by Automated Optical Analyzer Using Polarized Lightstandard by Technical Association of the Pulp and...

TAPPI T 551 om-23

TAPPI T 551 om-23

Thickness of Paper and Paperboard (Soft Platen Method)standard by Technical Association of the Pulp and Paper Industry, 06/01/2023

Back to Top